鎂合金犧牲陽極高電位鎂合金犧牲陽極廣泛用于石油管道、天燃氣、煤氣管道和儲罐；港口、海底管線、鉆井平臺；機場、發電廠、市政建設、水處理廠、石化工廠、冶煉廠、加油站的腐蝕防護等設備。
鎂陽極的優點：對鋼鐵陰極保護（-0．85V）的激勵電壓力-0.7V左右，適應的土壤電阻率范圍廣，陽極表面不極化，腐蝕產物易脫落。

詳細介紹

物超所值的成套的鎂陽極價格

Price of Magnesium anode sets with value exceeding value

成套鎂犧牲陽極構成

由鎂犧牲陽極錠1支，一根VV-10㎜2電纜3米，填包料50kg，棉布口袋1條，塑料編織袋1條組成。

即棉布口袋內有鎂犧牲陽極錠1支其鐵芯上焊VV-10㎜2電纜3米1根，焊接處做絕緣處理，并套有熱縮管。鎂犧牲陽極錠周圍均勻分布50kg填包料。棉布口袋外套塑料編織袋1條?！?/span>

鎂犧牲陽極適用于在土壤、淡水及海水等介質中工作的鋼質設施的陰極保護。

陽極安裝前準備

在組裝犧牲陽極之前，應檢驗陽極表面是否有油污和氧化物。犧牲陽極表面的油污和氧化物能降低陽極的活性，影響陽極電流的發生，所以陽極表面如存在油污和氧化物，應采用砂紙將陽極表面打磨干凈。填料包的組裝可在室內或現場進行，應保證陽極四周的填料厚度*、密實，各邊厚度不小于50mm。填料應調拌均勻，不得混入石塊、泥土、雜草等。每支陽極需用填料約50Kg

在腐蝕和防護研究中，致力于知識發展和傳播。腐蝕是材料受環境作而發生破壞或變質。材料包括金屬和非金屬材料。凡是使材料地方，都存在不同形式和不同程度腐蝕問題。每年腐蝕所造成經濟損失已超過火災、水災、地震和車禍損失總和。金屬氧化物陽有優異物理，化學和電化學性質。由于使鈦作為基材，因此易于加工成所需形狀并且重量輕，便于處理和安裝。我們公司采新研究方混合金屬氧化物陽極材料生產mmo電極。它利iro2 在酸性介質中具有高耐腐蝕性，同時還考慮到氧化釕iro2電*氧析過電位，并加入iro2和sno2，ruo 2，ta2o5，pdo等形成復合金屬氧化物。電極，金屬氧化物陽有形狀...... 對于已建平臺，水下安裝犧牲陽極費高昂，上述固定式也因為安裝費太高，無法采。張緊式外加電流陰極保護，兼具陰極保護和監測功能。輔助陽極、參比電極和電纜集成于一體，稱之為復合電纜，具有承重、供給陽極電流和傳輸監測功能。復合電纜頂部固定在平臺桿件上，底部固定在重力基礎上，并根據海況條件施加一定預張力，使其處于張緊狀態，所以也稱為拉伸式外加電流陰極保護。重力基礎結構和重量、復合電纜張緊力等需要考慮具體條件、水深等多因素來確定，同時要保證在可能條件，特別是條件下，復合電纜與平臺結構件、及復合電纜之間保持一定距離。復合纜結構和長度、重力基礎及張緊力之間密切相關，設計時需要統一考慮。因為輔助陽極垂直均勻布置，因此，電位分布更均勻，所需保護電流也相對較小。該大特點在于安裝時不需水下作業，或只需簡單水下作業作為輔助，因此便于安裝，整體成本低，于在役平臺陰極保護服役具有非常大優勢。

Reference electrodes and cables are integrated into one, called composite cables, with load bearing, supply anode current and transmission monitoring functions. The top of the composite cable is fixed on the platform rod, the bottom is fixed on the basis of gravity, and a certain pre-tension is applied according to the sea conditions to make it in a tensioning state, so it is also called a tensile applied current cathode protection. Gravity infrastructure and weight, composite cable tensioning force and other factors need to be considered to determine the specific conditions, water depth and other factors, and at the same time to ensure that under possible conditions, especially extreme conditions, composite cables and platform structures, and composite cables maintain a certain distance. The structure and length of composite cable, gravity foundation and tension force are closely related. Because the auxiliary anode is evenly arranged vertically, the potential distribution is more uniform and the required protection current is relatively small. This major feature is that it does not require underwater operations during installation, or it only requires simple underwater operations as an aid. Therefore, it is easy to install, and the overall cost is low. It has a great advantage in serving the cathode protection of the active platform.

鎂陽極通常是加入鋁、鋅、錳的鎂合金。必須保持非常低的鎳、鐵、銅的含量，因為它們促進自腐蝕。如果鎳的含量超過百分之0.001，就損壞陽極特性。銅的影響不是太明顯。銅會增加自腐蝕，當含量達到百分之0.05時，如有百分之0.3的錳，則沒有有害影響。鐵含量大概在百分之0.01時，假如錳含量超過百分之0.3，不會增加自腐蝕。加入錳時，由于錳的覆蓋而形成鐵的晶體，這樣鐵從熔融狀態沉淀下來固化時不會產生有害影響。加入鋅可以使腐蝕性侵蝕更均勻，而且抑制了其他雜志的敏感性。鎂合金陽極電位負，單位質量發生電量大，是理想的犧牲陽極材料。適用于土壤、淡水及海水等介質中的金屬構筑物的陰極保護。鎂合金犧牲陽極按國標GB/T17731-2004鎂合金犧牲陽極生產，用于管道的陽極同時符合SY/T0019-97埋地鋼質管道犧牲陽極陰極保護設計規范。